Home > Carbon Steel Sheet >

Low Carbon Mild Steel Sheet Manganese Containing Excellent Machinability

Product Categories

Carbon Steel Sheet [24]
Carbon Steel Round Bar [31]
Carbon Steel Flat Bar [24]
Stainless Steel Sheet Metal [88]
Wear Resistant Steel Plate [30]
Galvanized Steel Coil [36]
Alloy Steel Products [44]
Carbon Steel Channel [20]
Carbon Steel Square Tube [16]
Stainless Steel Strip Coil [51]
Stainless Steel Round Bar [28]
Hardened Spring Steel [14]
Galvanised Corrugated Roofing Sheets [20]
Steel Chequered Plate [10]
PPGI Steel Coil [25]
Custom Steel Fabrication [12]
Carbon Steel Coil [9]
Aluminium Alloy Sheet [12]

Wuxi Jinlai Mechanical Processing Co., Ltd.

Contact Now

Low Carbon Mild Steel Sheet Manganese Containing Excellent Machinability

Name: Low Carbon Mild Steel Sheet Manganese Containing Excellent Machinability
Brand: JIN LAI
Price: 1 USD

Brand Name : JIN LAI

Model Number : A572 Grade 50

Certification : ISO BV

Place of Origin : China

MOQ : 1 ton

Price : negotiation

Payment Terms : T/T, Western Union

Supply Ability : 5000 tons per month

Delivery Time : ship withon 10 days after receive the advance

Packaging Details : standard packing or as the requirement

Length : 4-11M OR As requirement

surface : oil,black,galvanized

Packing : Standard seaport packing

Width : 1000-2200mm

Standard : AISI, ASTM, BS, DIN, GB, JIS

Material : C22 C25 C30 C35

Thickness : 1.5-380mm

Technique : Hot rolled

Contact Now

The plates are made up of the excellent quality alloys that have great forming and welding properties. Plus, they are energy efficient and have the ability to payload higher therefore it is widely used in the linear structures. Some of the common applications where EN 10025-2 S690QL Tempered and Quenched Plate, is largely used are heavy transportation, lifting equipment, machine building, etc. On the other hand, some of the popular industries where it is used are petrochemical industries, chemical industries, fertilizer industries, power generation industries, nuclear industries, etc. The features offered by these amazing plates are- higher reliability, higher weldability capacity, easy to install in several small and big industries, easy to fabricate, excellent formability, toughness, it is a strong plate that can e utilized in the higher as well lower temperature conditions.

EN 10025-2 S690QL Steel PLATES higher strengthening properties and produces higher tensile, higher mechanical strength as well as higher-yielding strength when used in the different applications around the world. It also excites great resistance properties and some of them are corrosion resistance, oxidation resistance, pitting and crevice resistance, stress chloride cracking resistance, and many more. At Conquest Steel & Alloys we pack our product with higher quality packing substance in order to avoid any damage to the products. Additionally, we also conduct tests on them such as macro tests, hardness tests, micro tests, destructive tests, PMI tests, etc.

EN 10025-2 S690QL Steel Plate Specification :

Specification : ASTM A514/A514M-13
Item : EN 10025-2 S690QL Quenched And Tempered Structural Steel Plate
Thickness : 3 - 200mm
Width : 500 - 3000mm

Length : 1000 - 12000mm

EN 10025-2 S690QL STRUCTURAL STEEL PLATE EQUIVALENT GRADES

Grade	Standards	Country
S690QL EN10137-2 EN10025-6:2004	EN	EUROPE
A709-100	ASTM	USA
TStE690V DILLIMAX 690 NAXTRA 70	DIN, WNr	GERMANY
E690T E690TFP S690T	AFNOR/ NF A36- 204	FRANCE
FeE690VKT	EN	EUROPEAN (OLD)
2625 WELDOX 700	SS	SWEDON
E690	ISO 4952	INTER
JFE HITEN 780LE	JIS	JAPAN
ALFORM 700		AUSTRIA

EN 10025-2 S690QL TEMPERED AND QUENCHED PLATE CHEMICAL COMPOSITION

C	Si	Mn	P	S	B	Cr	Cu	Mo	N	Nb*	Ni	Ti*	V*	Zr*
0.20	0.80	1.70	0.020	0.010	0.005	1.50	0.50	0.70	0.015	0.06	2.0	0.05	0.12	0.15

EN 10025-2 S690QL HIGH YIELD STRENGTH STEEL PLATES MECHANICAL PROPERTIES

Steel grade	Yield strength R_eH MPa	Tensile strength R_m MPa	EN 100256: 2004 + A1:2009	Heavy plate thickness mm	Obsolete standard EN 101372 1995	Elongation, min %
S690Q, QL	690	770 – 940	S690QL	6 – 60	S690QL	14

EN10025-2 S235J0

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.17	1.4	~	0.03	0.03	0.012	0.55
>40	0.17
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	235		360-510		17
>16, ≦100	225
>100	175		340-500

EN10025-2 S235JR

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.17	1.4	~	0.035	0.035	0.012	0.55
>40	0.20
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	235		360-510		17
>16, ≦100	215
>100	175		340-500

EN10025-2 S275JR

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.21	1.5	~	0.035	0.035	0.012	0.55
>40	0.22
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	275		410-580		15
>16, ≦100	235
>100	205		380-540

EN10025-2 S235J2

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.17	1.4	~	0.025	0.025	~	0.55
>40	0.17
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	235		360-510		15
>16, ≦100	225
>100	165		330-510

EN10025-2 S275J2

Chemical composition % MAX
THICKNESS(MM)	C	Mn0	Si	P	S	N	Cu
≦40	0.18	1.5	~	0.025	0.025	0.012	0.55
>40	0.18
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	275		410-580		13
>16, ≦100	235
>100	195		410-580

EN10025-2 S275J0

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.18	1.5	~	0.03	0.03	0.012	0.55
>40	0.18
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	275		410-580		15
>16, ≦100	235
>100	205		380-540

EN10025-2 S355J0

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.20	1.6	0.55	0.03	0.03	0.012	0.55
>40	0.22
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	355		470-680		14
>16, ≦100	315
>100	275		450-600

EN10025-2 S355K2

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.20	1.6	0.55	0.025	0.025	~	0.55
>40	0.22
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	355		470-680		12
>16, ≦100	315
>100	265		450-600

EN10025-2 S355J2

Product Tags:

cold rolled mild steel sheet

low carbon steel plate

Chemical composition % MAX
THICKNESS(MM)	C	Mn	Si	P	S	N	Cu
≦40	0.20	1.6	0.55	0.025	0.025	~	0.55
>40	0.22
Mechanical properties MIN
	Yield Strength MPa		Tensile Strength MPa		Elongation in 2 in. %
≦16	355		470-680		14
>16, ≦100	315
>100	265

Low Carbon Mild Steel Sheet Manganese Containing Excellent Machinability Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Wuxi Jinlai Mechanical Processing Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!